百安涂料
NCB (HS) -2.5 indoor ultra-thin steel structure fire retardant coating
Application areas
Widely used in large industrial and mining steel plant, airports, power plants, petrochemicals, commercial plaza, all kinds of gymnasium, exhibition hall main steel structure fire protection.
Product Features
Easy construction, non-toxic
Thin coating, excellent fire performance;
High hardness film;
Coating excellent anti-aging properties, can maintain for many years not powder;
Construction technology
Process
Technical specifications
The main material
Substrate processing
Clean the surface of steel components foreign body and rust, metal surface treatment of oil, to rust Standard ST2
Rust primer repair
Brush or spray twice with water-based or oily rust-proof primer to repair surface rust-proof steel components
Lanling inorganic zinc-rich primer or BA-601D water-based primer
Fire paint construction
Modulation to the appropriate construction viscosity, spraying or brushing the way of construction, control the thickness of each coating to prevent cracking, after a period of time before coating, until the specified thickness
Contego thin fire retardant coating
note
Construction Conditions:
1, the construction environment temperature is 5-40 ℃, the substrate temperature is 5-45 ℃, the air relative humidity is not more than 90%;
2, Maintain air circulation at construction site with wind speed no more than 5m / s, and should not be used for construction when outdoor work or construction components dew condensation;
Technical Parameters
Test items
Technical indicators
The status in the container
After mixing was fine and delicate state, no caking
Drying time (dry table) / h
≤8
Appearance and color
After the coating is dry, the appearance and color of the same sample should be no significant difference
Initial dry crack resistance
No cracks should appear
Bond strength / MPa
≥0.2
Water resistance / h
≥24 coating should be no layer, foam, off phenomenon
Resistance to heat cycle / time
≥15 coating should be no cracking, peeling, foaming phenomenon
Fire resistance
Coating thickness / mm (not more than)
2.00 ± 0.02
Fire resistance / h (not less than) (made of I-beam made of 136b or 140b standard)
1.0